Granules FCer ZrO2

330,00 VAT not included

Quantity: 80 gr (Equivalent to 10 meter of  filament Ø=1,75 mm)

Short description: GRANULES-FCer ZrO2 is an easily printable feedstock with a high content of 3 mol.% yttria stabilized zirconia (Y-TZP) nanoparticles. After printing your desired shape, the sintering process provides you a 100% zirconia piece or scaffold.

Format: Plastic Jar

Granule & Printing: Granule diameter & fluency match the printing conditions hot-ends with pellets’ reservoir – Printing Temperature 158 -175ºC

Particle: Y-TZP Tosho Mean Diameter 675 nm – Inorganic Content: 44 vol.%.

Technical Data Sheet (TDS)

If you have a special request or need a personalized granule, please contact us!


Advantages: GRANULES-FCer ZrO2 can be sintered. Furthermore, it remains easily printable by FFF, without clogging problems. GRANULES-FCer ZrO2 is specifically formulated to allow 100% inorganic parts to be obtained through 3D printing, allowing easy manufacturing of pieces with custom shapes.


Storage Conditions
-Keep in a dry place
-Protect from direct sunlight
-Storage between 5ºC- 30ºC


Granule Characteristics
Material: Zirconium Oxide
Composition: 44 vol.%


Physical Propierties
Glass Transition Temp. (Tg): 53 ºC
Melting Temp: 153 ºC
Sintering Temp.: >98.5% after 1500ºC


Printing Recommendations
Printing Temp: 158 – 175 ºC
Hot Pad: 30 – 60 ºC
Printing Speed: 20 mm/s
Layer Height > 0.2 mm


Particle Properties
Particle: Y-TZP Tosho
Size (Dv50): 675 nm
Density: 6.03 g / cm³
Spec Surf. Area: 6.70 m2 /g