Granules FCer WC-Ni

360,00 VAT not included

Quantity: 175 gr (Equivalent to 10 meter of  filament Ø=1,75 mm)

Short description: GRANULES FCer WC-Ni is an easily printable feedstock with a high content of a sinterable mixture of Tungsten Carbide and Nickel nanoparticles. After printing your desired shape, the sintering process provides you a 100% hardmetal piece or scaffold.

Format: Plastic Jar

Granules size & fluency match the printing conditions of hot-ends with pellets’ reservoir- Printing Temperature 160 -170ºC

Particles: WC (d50=4.9µm)  and Ni (d50=300 nm) – Inorganic Content: 45 vol.%.

 

If you have a special request or need a personalized filament, please contact us!

Category:
Description

Advantages: Granules FCer WC-Ni is a composite feedstock that can be sintered in conventional vacuum furnaces. Furthermore, it remains easily printable by screw FFF, without clogging problems. Granules FCer WC-Ni is specifically formulated to manufacture hard-metal parts through 3D printing, allowing easy manufacturing of dense pieces and scaffolds with custom shapes. Sintering of the printed composite in conventional vacuum furnaces yields to  100% hardmetal parts.

 

Storage Conditions
-Keep in a dry place
-Protect from direct sunlight
-Storage between 5ºC and 30ºC

 

Granules Characteristics
Material: Tungsten Carbide with 9 wt.% (15 vol.%) of nanosized Nickel
Composition: 45 vol.% (91 wt.%)
Format:  Plastic Jar

 

Physical Properties
Glass Transition Temp. (Tg): – ºC
Melting Temp: 150 ºC
Sintering Temp.: 1550ºC (99 th.%) under vacuum

 

Printing Recommendations
Printing Temp: 160 – 170 ºC
Hot Pad: 30 – 60 ºC
Printing Speed: 10-20 mm/s
Layer Height: ≥ 0.15 mm
Nozzle Diameter: ≥ 0.4 mm

 

WC Particles
Size (Dv50): 4,7 µm
Density: 15.63 g / cm³
Spec Surf. Area: 0.24 m2 /g

 

Nickel Particles
Size (Dv50): 370 nm
Density: 8.91 g / cm³
Spec Surf. Area: 1.80 m2 /g