FCer ZrO2 (1,75mm/10m)

330,00 VAT not included

Price: €/10m

Linear Density: 8.1 g/m

Short description: FILAMENT-Cer ZrO 2 is an easily printable filament with a high content of 3 mol.% yttria stabilized zirconia (Y-TZP) nanoparticles. After printing your desired shape, the sintering process provides you a 100% zirconia piece or scaffold.

Filament & Printing: Filament Diameter 1.75 mm (±0.15 mm) – Printing Temperature 158 -170ºC

Particle: Y-TZP Tosho Mean Diameter 400 nm – Inorganic Content: 44 vol.%.


Technical Data Sheet (TDS)

If you have a special request or need a personalized filament, please contact us!

Categories: ,

Advantages: FILAMENT-Cer ZrO2 can be sintered. Furthermore, it remains easily printable by FFF, without clogging problems.

Applications: FILAMENT-Cer ZrO2 is specifically formulated to allow 100% inorganic parts to be obtained through 3D printing, allowing easy manufacturing of dense pieces and scaffolds with custom shapes.


Storage Conditions
-Keep in a dry place
-Protect from direct sunlight
-Storage between 5ºC and 30ºC


Filament Characteristics
Material: Zirconium Oxide
Composition: 44 vol.% (79 wt.%)
Diameter: 1.75 mm (±0.15 mm)
Linear Density: 8.1 g/cm
Format:  Spool vacuum packed
Sintering Temp.: 1550ºC (99 th.%)


Physical Propierties
Glass Transition Temp. (Tg): 60 ºC
Melting Temp: 154 ºC


Printing Recommendations
Printing Temp: 158 – 170 ºC
Hot Pad: 30 – 60 ºC
Printing Speed: 10-20 mm/s
Layer Height: ≥ 0.2 mm
Nozzle Diameter: ≥ 0.4 mm


Particle Properties
Particle: Y-TZP Tosho
Size (Dv50): 400 nm
Density: 6.05 g / cm³
Spec Surf. Area: 6.70 m2 /g